Farbe | braun, Orange, schwarz |
---|---|
Material | phenolic+cotton |
Oberfläche | Schlank |
Zugfestigkeit | 78Mpa |
Kompressions-Stärke | 138Mpa |
Material | 100%virgin PP material |
---|---|
Color | white,grey,black |
Working Temperature | -25℃-+90℃ |
Density | 0.93g/cm³ |
Outside diameter | od10-400mm |
Material | Nylon PA6 material |
---|---|
Color | ivory,blue,black,green |
Tensile Strength | 90Mpa |
Bending Strength | 155Mpa |
Density | 1.16g/cm³ |
Material | Phenolic+cotton |
---|---|
Color | brown,orange,black |
Surface | smooth |
Tensile Strength | 78Mpa |
Compression Strength | 138Mpa |
Material | Phenolic+cotton |
---|---|
Color | brown,orange,black |
Surface | smooth |
Tensile Strength | 78Mpa |
Compression Strength | 138Mpa |
Material | 100%virgin PP material |
---|---|
Color | white,grey,black |
Working Temperature | -25℃-+90℃ |
Density | 0.93g/cm³ |
Outside diameter | od10-400mm |
Material | 100% reines Polyäther, Polyester oder TPU |
---|---|
Erzeugnis | formen Sie oder verdrängen Sie |
Farbe | transparentes, Orangen-, Blaues, Schwarzesetc. |
Zugfestigkeit | 30-55Mpa |
Härte | 80-90shore A |
Material | phenolic+cotton |
---|---|
Farbe | braun, rot, beige, gelb |
Oberfläche | Schlank |
Zugfestigkeit | 78Mpa |
Abbruchspannung | 10KV |
Material | 100% Jungfraupolyäther, Polyester |
---|---|
Farbe | gelb, braun, schwarz, rot |
Akron-Abnutzungsverlust | <0> |
Kompressions-Satz | <10> |
Betriebstemperatur | Maximum 120°C |
Material | Phenolic+cotton |
---|---|
Color | brown,orange,black |
Surface | smooth |
Tensile Strength | 78Mpa |
Compression Strength | 138Mpa |